The effect of LaF3 nanocluster modified with succinimide on the lubricating performance of liquid paraffin for steel-on-steel system

LaF3 nanocluster modified with succinimide was prepared. The effect of the modified LaF3 nanocluster on the lubricating performance of liquid paraffin for steel-on-steel sliding system was investigated on a four-ball machine. The morphology of LaF3 and its lubricating mechanisms as additive in liquid paraffin were studied by means of transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). It was found that LaF3 nanocluster modified with succinimide as an additive in liquid paraffin increased the load-carrying capacity and had good antiwear and friction-reduction behaviour. The XPS analysis of the worn steel surfaces indicated that a boundary lubricating film consisting of physically adsorbing film (succinimide) and tribochemically reacting film (lanthanum oxide and ferrous fluoride) was generated during the friction process. This contributed to improving the lubricating performance of liquid paraffin.