Chemical analysis of wear tracks on magnetic disks by TOF-SIMS

Surface reactions on magnetic recording disks have been studied during sliding with ceramic sliders in the main chamber of TOF-SIMS. Chemical change of lubricant oil in the wear track was observed by the chemical image of TOF-SIMS. The magnetic disk surface was covered with perfluoroalkyl polyether lubricant (Fomblin Zdol). The Si tip slider surface was covered with Al2O3, DLC, TiN or c-BN coating. Experimental conditions were as follows: 0.8 mN of load and a sliding speed of 0.01 m/s. Lubricant oils were decomposed with Al2O3 and TiN slider surfaces. Metal (Al, Ti) fluorides were detected by TOF-SIMS in the sliding track. Material transfer occurred by chemical wear of slider material. From TOF-SIMS observation, the decomposition of lubricant molecules was initiated at the end group of molecules (-CF2CH2OH). On the other hand, DLC and c-BN sliders suppressed the decomposition reaction of PFPE oils. In conclusion, hard and chemical inert materials such as DLC and c-BN are suitable for a long-life HDI.