Characterisation of DLC coating adherence by scratch testing

In order to characterize the adherence of DLC coatings (Diamond Like Carbon), scratch testing was performed on a unit equipped with sensors for normal and tangential forces, and an acoustic detector to detect the nucleation and the propagation of cracks. The system is also equipped with a microscope permitting observation of each event on the scratch according to the friction tangential force signal or the acoustic signal. The local microscopic observation allows identification of the damage with respect to the normal load. The test was performed with a Rockwell C indenter at the relative displacement speed, v=10 mm/min under a progressive normal load from 5 to 55 N. g failure appears in various modes, particularly the following: propagation of the cracks along the longitudinal edges of the scratch; propagation in front of the indenter; rupture along the maximum principal stress lines; and, detachment in the subsurface by shearing of the coating. The microscopic analysis of the evolution of the scratch under a progressive normal load permits identification of the various traces and the damage mechanisms of the coating. s study, experimental results are shown for the scratch tests on bulk glass and DLC coating. Various modes of crack initiation, damage and rupture of these materials according to the critical normal load are presented. The analysis of the contact stress field distribution in bulk glass enables identification of the crack initiation and its propagation in the coating.