Sliding wear transition for the CW614 brass alloy

Dry sliding wear tests were performed on a CW614 brass alloy using a pin-on-ring configuration. Wear kinetics were measured within a load range of 20–80 N and sliding velocity ranging from 1 to 7 m/s. Chemical compositions, morphologies and microstructures of worn surfaces and wear debris were characterised by scanning electron microscope (SEM) and energy dispersive X-ray spectrometer (EDS). Two main wear regimes have been observed: severe wear and mild wear. The results of wear tests and metallographic investigations on worn surfaces have been summarised in a wear mechanism map. It was found that the wear transition is controlled by a critical temperature at the contact surface.