Thermal stability and high-temperature wear of Ti–TiN and TiN–CrN nanomultilayer coatings under self-mated conditions

Ti–TiN and TiN–CrN nanomultilayers were thermally stable retaining uniform and sharp layer interfaces up to 24 h at 773 K, without any oxidation or phase transformation accompanying each individual layer. Decreasing the multilayer spacing resulted in an increase in the hardness in both cases. The coating hardness was found to be independent of the substrate type, when applied on HS718, Ti64 and HCHCr substrates. In scratch testing, the multilayers displayed a better resistance to the onset of failure, as compared to the monolayer TiN. The substrate plasticity played an important role in determining the coating failure mode. Self-mated wear tests revealed the CrN–TiN system to exhibit the best wear behaviour, both at room temperature and at 773 K. The Ti–TiN coatings are more accommodative with all three substrates, as compared to TiN–CrN and TiN.