Effects of carbon fiber length on the tribological properties of paper-based friction materials

Four kinds of paper-based friction materials reinforced with carbon fibers of 100, 400, 600 and 800 μm were prepared by paper-making processes. Experimental results showed that the friction materials became porous with fiber length increasing. The friction torque curves were flat except the sample with 100 μm fibers. The wear rate of the sample with 100 μm fibers was only 1.40×10−5 mm3/J. Tiny debris and fine scratches formed in the worn surface were the reason for excellent wear resistance of friction pairs with 100 μm fibers. The friction pairs with 400, 600 and 800 μm fibers showed typically abrasive wear and fatigue wear.