XPS study and physico-chemical properties of nitrogen-enriched microporous activated carbon from high volatile bituminous coal

N-enriched microporous active carbons of different physico-chemical parameters have been obtained from high volatile bituminous coal subjected to the processes of ammoxidation, carbonisation and activation in different sequences. Ammoxidation was performed by a mixture of ammonia and air at the ratio 1:3 (flow ratio 250 ml/min:750 ml/min) at 350 °C, at each stage of production i.e. that of precursor, carbonisate and active carbon. Ammoxidation performed at the stage of demineralised coal or carbonisate has been shown to lead to a significant nitrogen enrichment and to have beneficial effect on the porous structure of the carbon during activation, allowing obtaining samples of the surface area of 2600–2800 m2/g and pore volume 1.29–1.60 cm3/g to be obtained with the yield of about 50%. The amount of nitrogen introduced into the carbon structure was found to depend on the sequence of the processes applied. The greatest amount of nitrogen was introduced for the processes in the sequence carbonisation → activation → ammoxidation. The introduction of nitrogen at the stage of active carbon leads to a reduction in the surface area and lowering of its sorption capacity. From the XPS study, ammoxidation introduces nitrogen mainly in the form of imines, amines, amides, N-5 and N-6, irrespective of the processing stage at which it is applied.