Improvement of a-Si solar cell properties by using SnO2:F TCO films coated with an ultra-thin TiO2 layer prepared by APCVD
Author/Authors :
Kambe، نويسنده , , M. and Fukawa، نويسنده , , M. and Taneda، نويسنده , , N. and Sato، نويسنده , , K.، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2006
Abstract :
TiO2-overcoated SnO2:F transparent conductive oxide films were prepared by atmospheric pressure chemical vapor deposition (APCVD) and an effect of TiO2 layer thickness on a-Si solar cell properties was investigated. The optical properties and the structure of the TiO2 films were evaluated by spectroscopic ellipsometry and X-ray difractometry. a-Si thin film solar cells were fabricated on the SnO2:F films over-coated with TiO2 films of various thicknesses (1.0, 1.5 and 2.0 nm) and I–V characteristics of these cells were measured under 1 sun (100 mW/cm2 AM-1.5) illumination. It was found that the TiO2 film deposited by APCVD has a refractive index of 2.4 at 550 nm and anatase crystal structure. The conversion efficiency of the a-Si solar cell fabricated on the 2.0 nm TiO2-overcoated SnO2:F film increased by 3%, which is mainly attributed to an increase in open circuit voltage (Voc) of 30 mV.
Keywords :
Transparent conductive oxide , Titanium oxide , Open circuit voltage
Journal title :
Solar Energy Materials and Solar Cells
Journal title :
Solar Energy Materials and Solar Cells