Reaction-sintering of intermetallic alloys of the Ni–Al–Mo system

A powder metallurgy route has been used for producing binary and ternary alloys of the Ni–Al–Mo system. Elemental powder mixtures were compacted and, then, sintered in a dilatometer. In this way the dimensional changes involved with thermally induced transformations could be followed during continuous heating runs up to the sintering temperatures. Sintering was assisted by the formation of a liquid phase, promoted by the heat output coming from the intermetallic phase formation reactions. The amount of liquid phase and the efficiency of sintering was highly dependent on the heating rate. A threshold value for optimal densification was identified for some compositions. The effect of other processing parameters, such as pre-sintering compaction pressure and sintering atmosphere has been considered too. The characterisation of the final products was mainly based on X-ray diffraction analyses. The microstructural parameters and the phase composition of the sintered materials were evaluated. On the basis of these results it is possible to draw some conclusions concerning the main phenomena occurring during the sintering process.