Low-temperature brazing of titanium by the application of a Zr–Ti–Ni–Cu–Bebulk metallic glass (BMG) alloy as a filler

Titanium (Ti) was successfully brazed at low temperatures below 800 °C by employing a Zr41.2Ti13.8Ni10.0Cu12.5Be22.5 (at.%) bulk metallic glass (BMG) alloy as a filler. Through the use of this alloy filler, the detrimental segregation of Zr–Cu–Ni filler elements was completely eliminated by heating to well below 800 °C, so the resultant joint was quite homogeneous with a coarse acicular structure. The disappearance of the Zr–Cu–Ni segregated region was rate-controlled by the diffusion of the filler elements in the Ti base metal. Remarkably, the mechanical property and corrosion resistance of the homogeneous joint brazed at 800 °C for 10 min were mostly comparable to those of bulk Ti.