Martensitic transformation behavior of Ti–Ni–Ag alloys

Microstructures and martensitic transformation behavior of Ti–Ni–Ag alloys prepared by arc melting were investigated by means of scanning electron microscopy (SEM), electron probe micro analysis (EPMA), differential scanning calorimetry (DSC), X-ray diffraction (XRD) and thermal cycling tests under constant load. Ti–Ni–Ag alloys consisted of Ti–Ni–Ag matrices, Ti2Ni and TiAg phases. Ti–Ni–Ag matrices contained 0.27–0.52 at.% of solute Ag atoms depending on alloy compositions. The B2–B19′ transformation occurred in Ti–50.1Ni–0.7Ag, Ti–49.2Ni–0.9Ag, Ti–49.2Ni–0.6Ag and Ti–49.0Ni–0.7Ag alloys, while the B2-R-B19′ transformation did in Ti–47.5Ni–1.3Ag and Ti–44.4Ni–1.1Ag alloys. Thermo-mechanical treatment separated the B2-R from the R–B19′ transformation clearly and improved shape recovery by increasing the critical stress for slip deformation in a Ti–50.0Ni–0.7Ag alloy.