Synergetic effects of Y-zeolite and amorphous silica-alumina as main FCC catalyst components on triisopropylbenzene cracking and coke formation

The synergetic effects of HY-zeolite and silica-alumina (SA), as two major components of an FCC catalyst, on the cracking activity and coking tendency during catalytic cracking of 1,3,5-triisopropylbenzene (TiPB, as a resid representative) were studied. NaY-zeolite and SA were synthesized by hydrothermal and co-precipitation methods, respectively, and ammonium exchanged for three times at 80 °C. The catalysts were characterized by XRD, XRF, SEM, BET, AAS and ammonia TPD techniques. TiPB cracking was investigated on four different catalyst configurations including SA, Y-zeolite, SA.Y and SA-Y in a fixed bed reactor. SA.Y stands for physical mixture of equal amounts of Y-zeolite and SA. For SA-Y, a bed of SA was placed upstream of the same amount of Y-zeolite. The catalysts were in-situ activated at 475 °C and evaluated by TiPB cracking at 350 °C. The coke content of the catalyst beds, after 40 min cracking of TiPB, was estimated by TPO using an FT-IR gas cell. At 3 min time on stream, 5.2 times higher yield of benzene, as a deep cracking product, is observed on SA-Y as compared to SA.Y. The TiPB conversion decreases in the order of SA-Y > SA.Y > Y-zeolite ≫ SA. Furthermore, as compared to Y-zeolite, 24% lower coke is formed on SA-Y. Also CO evolution during TPO of coked SA-Y catalyst is about 24% lower than that of the coked zeolite. As a result, protecting of Y-zeolite by SA from direct exposure to resid feed enhances the cracking activity, decreases the tendency to coke formation and diminishes CO emission in the catalyst regeneration process.