Molecularly imprinted polymer coated on stainless steel fiber for solid-phase microextraction of chloroacetanilide herbicides in soybean and corn

A molecularly imprinted polymer (MIP) with metolachlor as template was firstly coated on stainless steel fiber through chemical bonding strategy to solve the fragility problem of silica fiber substrate for solid-phase microextraction. The surface pretreatment of stainless steel fiber and the polymerization conditions were investigated systematically to enhance the preparation feasibility and MIP coating performance, and then a porous and highly cross-linked MIP coating with 14.8-μm thickness was obtained with over 200 times re-usability which was supported by non-fragile stainless steel fiber adoption. The MIP coating possessed specific selectivities to metolachlor, its metabolites and other chloroacetanilide herbicides with the factors of 1.1–4.6. Good extraction capacities of metolachlor, propisochlor and butachlor were found with MIP coating under quick adsorption and desorption kinetics, and the detection limits of 3.0, 9.6 and 38 μg L−1 were achieved, respectively. Moreover, the MIP-coated stainless steel fiber was evaluated for trace metolachlor, propisochlor and butachlor extraction in the spiked soybean and corn samples, and the enrichment factors of 54–60, 27–31 and 15–20 were obtained, respectively.