Solid surface mapping by inverse gas chromatography

Inverse gas chromatography (IGC) at infinite dilution, is a technique for characterising solid surfaces. Current practice is the injection of n-alkane homologous series to obtain the free energy of adsorption of the CH2 group, from which the London component of the solid surface free energy, γ S d , is calculated. A value around 40 mJ/m2 is obtained for poly(ethylene), and 30 mJ/m2 for a clean glass fibre, while the potential surface interactivity of a glass fibre is far greater than that of poly(ethylene). A specific component of the surface, in mJ/m2, should be calculated in order to obtain significant parameters. As applied up to date, when calculating the specific component of the surface energy, the fact that W a sp energy values are in a totally different scale than AN or DN values is a major drawback. Consequently, Ka and Kb values obtained are in arbitrary energy units, different from those of the London component measured by injecting the n-alkane series. This paper proposes a method to obtain Ka and Kb values of the surface in the same energetic scale than the London component. The method enables us to correct the traditional London component of a solid, obtaining a new value, where the amount of W a   C H 2 accounting for Debye interactions with polar sites, is excluded. As a result, an approach to surface mapping is performed in several different substrate materials. We show results obtained on different solid surfaces: poly(ethylene), clean glass fibre, glass beads, chemically modified glass beads and carbon fibre.