Effect of borate concentration on solidification of radioactive wastes by different cements

To investigate the effect of borate on the cementation of radioactive evaporator concentrates, and to provide more data for solidification formula optimization, the simulated borate evaporator concentrates with different borate concentrations (as B) and Na/B ratio (molar ratio) were solidified by sulfoaluminate cement (SAC) and Portland cement (PC), with addition of Ca(OH)2, zeolite and accelerator or water reducer. The hydration products of solidified matrices were characterized by X-ray diffraction (XRD). The experimental results showed that borate retarded the cement setting for both SAC and PC formulas, and the final setting time prolonged with decrease of Na/B ratio. Borate could enhance the fluidity of the cement mixture. The 28 d compressive strengths of the solidified matrices for both SAC and PC formulas decreased with increase of borate concentration. The XRD patterns suggested that, in the matrices maintained for 28 d, borate did not interfere with the formation of main hydration products of SAC and PC. Borate, in the form of B(OH)4−, incorporated in ettringite (3CaO·Al2O3·3CaSO4·32H2O) as solid solution phase. The formula of SAC and PC developed in this study was effective for cementation of the simulated borate evaporator concentrates. However further optimization was required to reduce retarding effect of higher borate concentrations and to extend the practical feasibility for actual evaporator concentrates.