Structural integrity assessment of the reactor pressure vessel under the pressurized thermal shock loading

Fracture mechanics analysis of pressurized thermal shock (PTS) is the key element of the integrity evaluation of the nuclear reactor pressure vessel (RPV). While the regulation of 10 CFR 50.61 and the ASME Code provide the guidance for the structural integrity, the guidance has been prepared under conservative assumptions. In this paper, the effects of conservative assumptions involved in the PTS analysis were investigated. The influence of different parameters, such as crack size, cladding effect and neutron fluence, were reviewed based on 3-D finite element analyses. Also, the sensitivity study of elastic–plastic approach, crack type and cladding thickness were reviewed. It was shown that crack depth, crack type, plastic effect and cladding thickness change the safety margin (SM) significantly, and the SM at the deepest point of the crack is not always smaller than that of the surface point, indicating that both the deepest and surface points of the crack front should be considered. For the reference transient, deeper cracks always give more conservative prediction. So compared to the prescribed analyses of a set of postulated defects with varying depths in the ASME code, it only needs to assess the crack with maximum depth in the code for the reference transient according to the conclusions.