Gelatinization mechanism of potato starch

The non-Newtonian behavior and dynamic viscoelasticity of potato starch (Jaga kids red ’90, 21.0% amylose content) solutions after storage at 25 and 4°C for 24 h were measured with a rheogoniometer. The flow curves, at 25°C, of potato starch showed plastic behavior >1.0% (w/v) after heating at 100°C for 30 min. A gelatinization of potato starch occurred above 1.0% at room temperature. A very large dynamic viscoelasticity was observed when potato starch solution (3.0%) was stored at 4°C for 24 h and stayed at a constant value with increasing temperature. A small dynamic modulus of potato starch was observed upon addition of urea (4.0 M) at low temperature (0°C) even after storage at 25 and 4°C for 24 h. A small dynamic modulus was also observed in 0.05 M NaOH solution. Possible models of gelatinization and retrogradation mechanism of potato starch were proposed.