Preparation and properties of glycerol plasticized-pea starch/zinc oxide-starch bionanocomposites

A bionanocomposite was cast using ZnO nanoparticles stabilized by soluble starch (nano-ZnO) as filler in a glycerol plasticized-pea starch (GPS) matrix. According to the characterization of nano-ZnO particles by Fourier-transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TG) and transmission electron microscopy (TEM), ZnO nanoparitlces (70 wt%) were encapsulated by starch (30 wt%) in nano-ZnO particles of about 10 nm. In GPS/nano-ZnO nanocomposites, loading a low level of nano-ZnO particles improved the pasting viscosity, storage modulus, glass transition temperature and UV absorbance. When the nano-ZnO content varied from 0 to 4 wt%, the tensile yield strength and Young’s modulus increased from 3.94 to 10.80 MPa and from 49.80 to 137.00 MPa, respectively. The water vapor permeability decreased from 4.76 × 10−10 to 2.18 × 10−10 g m−1 s−1 Pa−1. The improvement in these properties may be attributed to the interaction between the nano-ZnO filler and GPS matrix.