Synthesis and characterization of a novel super-absorbent based on chemically modified pulverized wheat straw and acrylic acid

In order to develop an eco-friendly polymer, the material was prepared from pulverized wheat straw by chemical methods. And a super-absorbent hydrogel has been synthesized with chemically modified pulverized wheat straw (CMPWS) and acrylic acid (AA) in aqueous solution. Factors, such as weight ratio of AA to CMPWS, the amount of initiator and cross-linker, temperature and neutralization degree of AA that influence absorbencies of super-absorbent were investigated. Moreover, the super-absorbent had been proved with expectant polymerization structure and good thermo-stability via IR spectrum and TGA analysis. The morphological features were evidenced by SEM images. The excellent product was obtained with the absorbencies of 417 g/g in distilled water and 45 g/g in 0.9 wt% NaCl solution.