Finishing of cotton fabrics with poly (N-vinyl-2-pyrrolidone) to improve their performance and antibacterial properties

Cotton fabric was thermally crosslinked with poly (N-vinyl-2-pyrrolidone) (PVP) at different conditions including temperature, time, PVP concentrations and molecular weights. Results indicated that treating the cotton fabrics with 4% aqueous solution of PVP of molecular weight 10,000 Dalton followed by drying at 85 °C for 5 min then curing at 160 °C for 3 min results in crosslinking as will as an improvement in some performance properties of that fabrics such as resiliency, tensile strength, and acid dyeability. Post-treating PVP crosslinked fabric with 5% iodine in ethanol solution for 5 h at 50 °C imparts antibacterial activity against Staphylococcus aureus and Escherichia coli. Moreover, incorporation of PVP in the easy-care finishing of cotton fabrics, as polymer additive, with N,N-dimethylol 4,5-dihydroxyethylene urea as a crosslinker enhances some of the performance properties of finished fabrics such as the nitrogen content, tensile strength and acid dyeability along with decreasing resiliency as well as whiteness index, whereas the ester crosslinking with citric acid, in presence of PVP, enhances resilience, tensile strength and whiteness indices accompanied with a reduction in the %N of the treated fabrics. Infra red spectrum of PVP crosslinked fabric as well as EDX analysis of loaded iodine on PVP crosslinked cotton fabric were investigated.