Enhancing antimicrobial properties of dyed and finished cotton fabrics

1,2,3-Benzothiazole-7-thiocarboxylic acid-S-methylester (commercially known as Actigard® AM-87) was utilized to impart cotton fabric durable antimicrobial properties. Finishing treatment was carried out under a variety of conditions. The latter were included, effect of pH, concentration of antibacterial agents, curing temperature and curing time. The effect of fabric construction, mercerization, and dyeing with different dyestuff were also investigated. The study was also extended to investigate the technical feasibility of combining antimicrobial finishing treatment in question with other finishing treatment generally carried out on cotton fabric, like soft finishing and crease recovery finishing. The treated fabrics were monitored for antimicrobial properties before and after washing. The treated fabrics were also evaluated for the physio-mechanical properties like fabric tensile strength, elongation at break (or bursting strength for knitted fabric), wettability, crease recovery angle, whiteness index and roughness. Results obtained show that, the most appropriate conditions for treatment cotton fabric with Actigard® are: padding the cotton fabric in aqueous solution containing 6% Actigard® at pH 5 (adjusted using formic acid) then squeezed to wet pick up of 100%, dried at 80 °C for 5 min then cured at 100 °C for 150 s. The untreated cotton fabric did not show any antimicrobial activity towards Staphylococcus aureus or Escherichia coli. Treatment of cotton fabric with Actigard® improves its antimicrobial properties towards S. aureus or E. coli. It is also observed that, treatment of cotton fabric with Actigard® marginally decreases fabric tensile strength, elongation at break, roughness and WI, whereas; both wettability and crease recovery angle remain practically intact. This was observed whether the fabric was pre-mercerized or not.