Synthesis and properties of carboxymethylchitosan hydrogels modified with poly(ester-urethane)

Preparation and properties of carboxymethylchitosan (CMC) modified with polyurethane (PU) containing poly(ethylene adipate) (PEA) as a soft segment is described. Urethane prepolymer was first synthesized by the reaction of PEA with an excess of 1,6-hexamethylene diisocyanate (HDI) to terminate its ends with isocyanate functional groups, followed by chain extension reaction using ethylene glycol as a chain extender. Its chemical structure was characterized by 1H NMR and FTIR, molecular weight by GPC, and thermal behavior by DSC. To prepare PU-modified CMC (CMC-PU), 1–60 wt% of PU were introduced into the CMC solution of THF:H2O mixture (50:50 v/v) in the presence of 10 wt% of hexamethylene-1,6-di-(aminocarboxysulfonate) (HDA) to increase network density. Formation of the network structure was confirmed by investigating percent crosslinking and water swelling properties of CMC-PU compared to CMC network without PU. When percent of PU increased from 1 to 60 wt%, percent crosslinking of CMC-PU gradually increased up to 82%, whereas equilibrium water content (EWC) dropped and retained at 1000%. SEM showed microphase separation of PU (10–50 μm) thoroughly dispersed in CMC surface and in the bulk. In addition, CMC-PU exhibited a slight enhancement in toughness properties. Cytotoxicity and biocompatibility tests indicated that CMC-PU was non-toxic.