Water interaction in paper cellulose fibres as investigated by NMR pulsed field gradient

In this paper, water diffusion coefficients were measured using NMR pulsed field gradient, on a variety of paper materials made from predominantly cellulose fibre and nanofibres, derived from wood, with different dimensions, internal porosity, and chemical composition. The moisture content ranged from 0.2 to 1.2 g of water/g of dry fibre. Diffusion measurements were made both in the plane and through the thickness of the sheet. All data was generally well fitted by a simple two component diffusion model. For moisture contents less than 0.55 and 0.85 g/g for measurements in the plane and through the thickness, respectively, it was found that both diffusion components increased approximately linearly with moisture content, with the faster diffusion coefficient being approximately five times larger than the smaller. The water appeared, within errors, to be evenly split between two components. The measured diffusion coefficients were not affected by fibre dimensions, internal structure or chemical composition, but were consistently higher when measured in the plane.