Influence of fly ash on strength and sorption characteristics of cold-bonded fly ash aggregate concrete

Cold-bonded fly ash aggregate concrete with fly ash as part of binder or fine aggregate facilitates high volume utilization of fly ash in concrete with minimum energy consumption. This paper investigates the influence of fly ash on strength and sorption behaviour of cold-bonded fly ash aggregate concrete due to partial replacement of cement and also as replacement material for sand. While cement replacement must be restricted based on the compressive strength requirement at desired age, replacement of sand with fly ash appears to be advantageous from early days onwards with higher enhancement in strength and higher utilization of fly ash in mixes of lower cement content. Microstructure of concrete was examined under BSEI mode. Replacement of sand with fly ash is effective in reducing water absorption and sorptivity attributable to the densification of both matrix and matrix–aggregate interfacial bond. Cold-bonded fly ash aggregate concrete with a cement content of 250 kg/m3, results in compressive strength of about 45 MPa, with a total inclusion of around 0.6 m3 of fly ash in unit volume of concrete.