Springback in acetylated wood based composites

Reasons of the strength loss of the acetylated wood based composites were still under question. This research was considered to study springback in the acetylated particleboard and the medium density fibreboard. Chips and fibres were acetylated by using the acetic anhydride to gain different percentages of the weights (WPG). The boards were made based on the target thicknesses. Thickness of the boards as well as the modulus of elasticity (MOE) and the modulus of rupture (MOR) were determined after conditioning based on three point static bending test. s showed that the moisture content and the thickness swelling of the boards were reduced as the WPG was increased. However, increase of the springback and reduction of the MOE and the MOR were revealed as the WPG increased in the test boards after condition. It was also revealed that the springback was correlated with the weight gain and increased as the WPG was raised in the test boards. Reduction of the MOE and the MOR was also correlated with the springback in the test boards.