Photoresponse of spray pyrolytically synthesized copper-doped p- thin film electrodes in water splitting

Stable Cu-doped iron (III) oxide thin film electrodes that exhibit p-type behavior were synthesized by a spray pyrolytic deposition (SPD) method on conducting tin oxide-coated glass substrates for photoelectrochemical water splitting. The highest photocurrent density of 0.94 mA / cm 2 was observed under an illumination intensity of 40 mW / cm 2 for Cu-doped samples prepared using an optimal 0.01155 M Cu 2 + at an optimal substrate temperature of 395 °C with a total spray time of 100 s at 0.0 V vs. SCE. These Cu-doped p- Fe 2 O 3 thin films were found to generate an optimum photoconversion efficiency of 1.3%. X-ray diffraction (XRD) data revealed that these films have mixed structures ( α - Fe 2 O 3 and CuFe 2 O 4 ). The Cu dopant level in p- Fe 2 O 3 was found to be 0.20% from X-ray photoelectron spectroscopic (XPS) data.