The stability of hydrogen evolution activity and corrosion behavior of NiCu coatings with long-term electrolysis in alkaline solution

In this study, NiCu composite coating was electrochemically deposited on a copper electrode (Cu/NiCu) and tested for hydrogen evolution reaction (HER) in 1 M KOH solution for long-term electrolysis with the help of cathodic current–potential curves and electrochemical impedance spectroscopy (EIS) techniques. The bulk and surface composition of the coating was determined using atomic absorption spectroscopy (AAS) and energy dispersive X-ray (EDX) analysis. The surface morphology was investigated by scanning electron microscopy (SEM). The effect of electrolysis on the corrosion behavior of the Cu/NiCu electrode was also reported. It was found that the NiCu coating had a compact and porous structure with good time stability. The HER activity of the coating was stable over 120 h electrolysis and the HER mechanism was not modified during the operation. The corrosion tests showed that the corrosion resistance of the Cu/NiCu electrode changed when a cathodic current was applied to the electrolysis system.