Self-humidification of a PEM fuel cell using a novel Pt/SiO2/C anode catalyst

In this work, a membrane electrode assembly (MEA) for proton exchange membrane fuel cell (PEMFC) operating under no external humidification has been successfully fabricated by using a composite Pt/SiO2/C catalyst at the anode. In the composite catalyst, amorphous silica, which originated from the hydrolysis of tetraethyl orthosilicate (TEOS), was immobilized on the surface of carbon powder to enhance the stability of silica and provide a well-humidified surrounding for proton transport in the catalyst layer. The characteristics of silica in the composite catalyst were investigated by XRD, SEM and XPS analysis. The single cell tests showed that the performance of the novel MEA was comparable to MEAs prepared using a standard commercial Pt/C catalyst with 100% external humidification, when both were operated on hydrogen and air. However, in the absence of humidification, the MEA using Pt/SiO2/C catalyst at the anode continued to show excellent performance, while the performance of the MEA containing only the Pt/C catalyst rapidly decayed. Long-term testing for 80 h further confirmed the high performance of the non-humidified MEA prepared with the composite catalyst. Based on the experimental data, a possible self-humidifying mechanism was proposed.