Effect of platinum doping of activated carbon on hydrogen storage behaviors of metal-organic frameworks-5

In this work, we prepared platinum doped on activated carbons/metal-organic frameworks-5 hybrid composites (Pt-ACs-MOF-5) to obtain a high hydrogen storage capacity. The surface functional groups and surface charges were confirmed by Fourier transfer infrared spectroscopy (FT-IR) and zeta-potential measurement, respectively. The microstructures were characterized by X-ray diffraction (XRD). The sizes and morphological structures were also evaluated using a scanning electron microscopy (SEM). The pore structure and specific surface area were analyzed by N2/77 K adsorption/desorption isotherms. The hydrogen storage capacity was studied by BEL-HP at 298 K and 100 bar. The results revealed that the hydrogen storage capacity of the Pt-ACs-MOF-5 was 2.3 wt.% at 298 K and 100 bar, which is remarkably enhanced by a factor of above five times and above three times compared with raw ACs and MOF-5, respectively. In conclusion, it was confirmed that Pt particles played a major role in improving the hydrogen storage capacity; MOF-5 would be a significantly encouraging material for a hydrogen storage medium as a receptor.