Author/Authors :
Kim، نويسنده , , Byung Hoon and Yun، نويسنده , , Yong Ju and Hong، نويسنده , , Won G. and Kim، نويسنده , , Chang-Hee and Lee، نويسنده , , Sang Moon and Yu، نويسنده , , Han Young and Kim، نويسنده , , Hae Jin، نويسنده ,
Abstract :
The high pressure H2 sorption isotherms for vanadium pentoxide foam (VOF) were obtained at a liquid nitrogen temperature. The enhancement of hydrogen storage capacity occurred in as-prepared VOF (∼1.0 wt%) in contrast to that in pristine vanadium pentoxide (∼0.2 wt%). The maximum capacity of hydrogen storage (∼2.0 wt%) was achieved by thermal annealing at Ta = 623 K. The enhancement of hydrogen storage in VOF is attributed to the morphological modulation by thermal annealing.