Towards the preparation of realistic model Ziegler-Natta catalysts: XPS study of the MgCl2/TiCl4 interaction with flat SiO2/Si(1 0 0)

Despite of the wide use of supported Ti based Ziegler-Natta catalysts in the olefin polymerization industry, questions concerning the role of each one of the catalyst components in the polymerization process, have not found a satisfactory answer yet. This is mainly because of the high sensitivity of these systems to oxygen and atmospheric moisture that makes their study in an atomic level rather complicated. Realistic surface science models of the pre-activated SiO2 supported MgCl2/TiCl4 and TiCl4 Ziegler-Natta catalysts were prepared by spin coating on flat conductive SiO2/Si(1 0 0) supports under inert atmosphere. This preparation technique resembles the wet chemical impregnation which is the industrial method of the catalyst preparation. XPS analysis showed that the catalyst precursor anchors on the silica surface through bonding of the Ti atoms with surface silanes or siloxanes, while Mg is attached to the Ti through chlorine bridges. Thermal treatment of the catalysts at 723 K leads to total Cl desorption when MgCl2 is not present while a significant amount of the Ti atoms is reduced to the Ti3+ state.