Surface structures formed by individual adsorption and coadsorption of Mn and Bi on Cu(0 0 1), studied by LEED

We have studied the individual adsorption of Mn and Bi, and their coadsorption on Cu(0 0 1) by low-energy electron diffraction (LEED). For Mn, we have determined the c(2 × 2) structure formed at 300 K, whose structure had been determined by several methods. We reconfirmed by a tensor LEED analysis that it is a substitutional structure and that a previously reported large corrugation (0.30 Å) between substitutional Mn and remaining surface Cu atoms coincides perfectly with the present value. In the individual adsorption of Bi, we have found a c(4 × 2) structure, which is formed by cooling below ∼250 K a surface prepared by Bi deposition of ∼0.25 ML coverage at 300 K where streaky half-order LEED spots appear. The c(4 × 2) structure has been determined by the tensor LEED analysis at 130 K and it is a substitutional structure. In the coadsorption, we found a c(6 × 4) structure, which has been determined by the tensor LEED analysis. It is very similar to the previously determined structure of the c(6 × 4) formed by coadsorption of Mg and Bi, and embedded MnBi4 clusters are arranged in the top Cu layer instead of MgBi4. Large lateral displacements of Bi atoms in the c(6 × 4)-(Mn + Bi) suggest that the Mn atoms undergo the size-enhancement caused by their large magnetic moment.