Aligning one-dimensional arrays of nanoclusters on a thin film of Al2O3 grown on vicinal NiAl surfaces

We present a self-organised approach for the synthesis of one-dimensional (1D) arrays of supported nanoclusters. By oxidising NiAl surfaces vicinal to the (1 0 0) plane tilted along the crystallographic direction [0 1 0], we produced ordered thin films of θ-Al2O3 that exhibit uniform protrusion stripes propagating uniquely along direction [0 0 1] of the NiAl. These protrusions are preferential centres for nucleation of metal deposited from a vapour; the nanoclusters grown from such metal are aligned and form massive 1D cluster arrays along direction [0 0 1]. The arrays of Co nanoclusters exhibit a diameter as small as 3 nm and length exceeding a micrometer. The results imply prospective applications for which a patterned assembly of nanoclusters is desired.