Gd adsorption on the Mo(2 1 1) surface

The adsorption of Gd thin layers on the Mo(2 1 1) face was investigated by using Auger electron spectroscopy (AES), low electron energy diffraction (LEED), scanning tunneling microscopy (STM), X-ray photoemission spectroscopy (XPS) and measurements of the work function changes (Δφ). It was found that at 300 K Gd does not form any dilute chain structures and from the very beginning of the adsorption process Gd forms a densely packed layer. The dilute p(4 × 1) chain structure was observed by LEED after annealing thin layers (θ < 1 ML) to temperatures above 770 K. STM images confirm the existence of the p(4 × 1) structure islands. The intermixing of the substrate and adsorbate atoms takes place.