Effects of surfactant/silica and silica/cerium ratios on the characteristics of mesoporous Ce-MCM-41

Using the surfactant CTMABr (cetyltrimethyl ammonium bromide) and cerium(IV) sulfate, mesoporous Ce-MCM-41 molecular sieves were produced under a hydrothermal condition with various surfactant/silica (surfactant/Si) and silica/cerium (Si/Ce) ratios. Changes to the structural traits caused by changing the molar ratios of both surfactant/Si and Si/Ce were investigated. XRD (X-ray diffraction), FT-IR (fourier transform infrared spectroscopy), and SEM (scanning electro microscopy) were used for the characterization of prepared mesoporous samples. Among the tested molar ratios, surfactant/Si ratio of 0.5 and 0.2 showed highest values of d1 0 0 and intensity, respectively, for the Si-MCM-41. XRD analysis also identified a quintessential hexagonal structure of Ce-MCM-41 for the Si/Ce molar ratio higher than 40 (maintaining the surfactant/Si ratio at 0.2). When cerium content was increased to have the Si/Ce molar ratio of 20, the hexagonal structure of Ce-MCM-41 was collapsed due to the structural stress of substituted cerium. FT-IR results confirmed calcination of Ce-MCM-41 and the incorporation of Ce4+ ions of cerium sulfate into the silica surface with proper removal of the surfactant. Rod-like shape with rounded edges of the prepared Ce-MCM-41 samples was identified by SEM. These results suggest surfactant/Si ratio of 0.2 and Si/Ce ratio of 40 for the production of Ce-MCM-41 with the highest level of crystallinity.