Conductivity/microstructure study of a pyrochlore-type ordered phase in the compound Zr0.75Ce0.08Nd0.17O1.92

The compound Zr0.75Ce0.08Nd0.17O1.92 was investigated as part of a much larger electrical conductivity/microstructure study of the systems ZrO2–CeO2–M2O3 (where M=Nd, Sm, …, Yb) [Solid State Ionics (2002)]. Electrical conductivity measurements performed in air at 800 °C showed significant conductivity degradation over a period of 200 h. Investigation of the annealed and as-fired specimens by ATEM revealed the presence of an emerging, ordered pyrochlore-type phase within the Zr0.75Ce0.08Nd0.17O1.92 defect-fluorite solid solution at much lower dopant levels than observed previously for zirconia binary systems.