Methane reforming to syngas over LaNixFe1−xO3 (0 ≤ x ≤ 1) mixed-oxide perovskites in the presence of CO2 and O2

The perovskite metal-oxides LaNixFe1−xO3 (0 ≤ x ≤1) were synthesized by a sol–gel method and investigated for the DR, POM, and CRM into synthesis gas. The catalysts were characterized by using XRD, BET, CA, SEM, EDS, HR-TEM, EDX and TPR in order to investigate the influence of the preparation parameters and evaluation condition. LaNi0.4Fe0.6O3 showed great stability, and fewer carbon deposits were detected on the spent catalyst after 1800 min evaluation on TOS. The effect of GHSV on the catalytic performance was investigated. The results obtained showed the H2/CO molar-ratio was around 0.9, 1.7, and 1.1 over different catalysts for DR, POM and CRM, respectively.