Oxygen diffusion in Sr3YCo4O10.5: An electrical conductivity relaxation and thermogravimetric analysis approach

Chemical oxygen diffusion coefficients and chemical surface exchange rates along with oxygen self-diffusion coefficients in dense samples of Sr3YCo4O10.5 + δ were studied by using a combination of electrical conductivity relaxation (ECR) measurements and thermogravimetric analysis (TGA) data in the temperature range of 650 °C–900 °C. Arrhenius behavior, A = A 0 exp − E A RT , was observed with activation energies of E A D chem = 1.16 ± 0.01 eV , E A D O = 1.56 ± 0.01 eV and E A k chem = 0.76 ± 0.05 eV for the chemical oxygen diffusion coefficient, the oxygen self-diffusion coefficient, and the chemical surface exchange rate, respectively. The thermodynamic factor changes with temperature from 611 at 650 °C to 177 at 900 °C.