Preparation of thin film of CaZrO3 by pulsed laser deposition
Author/Authors :
Joseph، نويسنده , , M and Sivakumar، نويسنده , , N and Manoravi، نويسنده , , P and Vanavaramban، نويسنده , , S، نويسنده ,
Issue Information :
دوهفته نامه با شماره پیاپی سال 2001
Abstract :
Thin films of CaZrO3 are prepared by pulsed laser deposition (PLD) using a 532-nm Q-switched Nd:YAG laser. Films prepared in vacuum, on annealing, revealed the structure of calcia stabilized zirconia, i.e. Ca0.15Zr0.85O1.85. Films prepared in the presence of 150×10−3 Torr of oxygen, on annealing, have CaZrO3 structure, though a small percentage of Ca0.15Zr0.85O1.85 is still present. Larger oxygen pressures during film deposition lead to the presence of many other oxides of a greater oxygen mole fraction in the film. Particulate deposition that leads to undesirable properties for the films is observed in the scanning electron microscopy (SEM) when the film is prepared using a laser fluence of the order of 16 J/cm2, whereas the fluence 0.64 J/cm2 produced particulate-free films. The vapor composition and the velocities of the different species (in vacuum) are determined using a quadrupole mass spectrometer (QMS), and the laser ablation process under the film deposition condition (laser fluence 0.64 J/cm2) is found to be thermal. The deficiency in Ca observed for the film prepared in vacuum appears to correlate with a deficiency in CaO+. The observed difference in the stoichiometry of the films deposited under vacuum and oxygen background is discussed based on the mass spectrometry results.
Keywords :
thin film deposition , Calcium zirconate , pulsed laser deposition , Laser vaporization
Journal title :
Solid State Ionics
Journal title :
Solid State Ionics