Reversible immobilization of catalase on fibrous polymer grafted and metal chelated chitosan membrane

Poly(itaconic acid) grafted and/or Fe(III) ions incorporated chitosan membranes were used for reversible immobilization of catalase (from bovine liver) via adsorption. The influences of pH and initial catalase concentration on the immobilization capacities of the CH-g-poly(IA) and CH-g-poly(IA)-Fe(III) membranes have been investigated in a batch system. Maximum catalase adsorption onto CH-g-poly(IA) and CH-g-poly(IA)-Fe(III) membrane were found to be 6.3 and 37.8 mg/g polymer at pH 5.0 and 6.5, respectively. The CH-g-poly(IA)-Fe(III) membrane with high catalase adsorption capacity was used in the rest of the study. The Km value for immobilized catalase on CH-g-poly(IA)-Fe(III) (25.8 mM) was higher about 1.6-fold than that of free enzyme (13.5 mM). Optimum operational temperature was observed at 40 °C, a 5 °C higher than that of the free enzyme and was significantly broader. The optimum operational pH was same for both free and immobilized catalase (pH 7.0). Thermal stability was found to increase with immobilization. Free catalase lost all its activity within 20 days whereas immobilized catalase lost 23% of its activity during the same incubation period. It was observed that the same support enzyme can be repeatedly used for immobilization of catalase after regeneration without significant loss in adsorption capacity or enzyme activity. In addition, the CH-g-poly(IA)-Fe(III) membrane prepared in this work showed promising potential for various biotechnological applications.