Strain-induced ordering of microdomain structures in polystyrene-block-polybutadiene-block-polystyrene triblock copolymers cross-linked in the disordered state

Strain-induced ordering of microdomain structures in cross-linked polystyrene-block-polybutadiene-block-polystyrene (SBS) triblock copolymers was examined by the small-angle X-ray scattering technique. To stretch the SBS samples at elevated temperature above the glass transition temperature of polystyrene, polybutadiene blocks were chemically cross-linked in the disordered state. The initial morphology was disorder-like or bicontinuous due to incompletion of microphase separation in the presence of the chemical cross-links. When the cross-linked SBS samples were mechanically stretched at 130 °C and were further annealed for 24 h under a stretched state, the random domain structures ordered gradually and lamellar-like regularity was finally attained. It was found that the ordering proceeded more for the case of the higher strain.