Oxygen permeation in bismuth-based materials. Part I: Sintering and oxygen permeation fluxes
Author/Authors
Capoen، نويسنده , , E. and Steil، نويسنده , , M.C. and Nowogrocki، نويسنده , , G. and Malys، نويسنده , , M. and Pirovano، نويسنده , , C. and Lِfberg، نويسنده , , A. and Bordes-Richard، نويسنده , , E. and Boivin، نويسنده , , J.C. and Mairesse، نويسنده , , G. and Vannier، نويسنده , , R.N.، نويسنده ,
Issue Information
هفته نامه با شماره پیاپی سال 2006
Pages
6
From page
483
To page
488
Abstract
Oxygen permeation measurements were performed on two layered bismuth based oxide ceramics: a rhombohedral phase belonging to the Bi2O3–CaO system, (Bi2O3)0.73–(CaO)0.27 (BICAO) and a BICOVOX phase. Oxygen permeability for these systems was compared to permeability of the cubic fluorite type structure with composition (Bi2O3)0.75(Er2O3)0.25 (BE25). Low oxygen permeability was observed for the pure ceramic. As for BE25, permeability was considerably increased if 40 vol.% of silver was added to BICAO. In contrast, permeability was not improved by addition of gold to BICOVOX. For this latter phase, the oxygen molecular exchange at the surface is clearly the limiting step in the oxygen transfer.
Keywords
Bismuth erbium oxide , Bismuth calcium oxide , BIMEVOX , Oxygen permeation