Synthesis, characterization, and properties of poly(ethylene terephthalate)/poly(1,4-butylene succinate) block copolymers

Reactive blending at 290 °C of a series of mixtures of poly(ethylene terephthalate) (PET) and poly(1,4-butylene succinate) (PBS) led to the formation of block PET/PBS copolyesters. The block lengths of the resulting copolymers decreased with the severity of the treatment. Copolyesters with PET/PBS molar compositions of 90/10, 80/20, 70/30, and 50/50 were prepared by this method and their composition and microstructure were characterized by 1H and 13C NMR, respectively. The Tg, Tm, and crystallinity of the copolymers decreased as the content in PBS and the degree of randomness increased. The elastic modulus and tensile strength of the copolymers decreased with the content of PBS, whereas, on the contrary, the elongation at break increased. The PET/PBS copolymers exhibited a pronounced hydrolytic degradability, which increased with the content in 1,4-butylene succinic units. Hydrolysis mainly occurred on the aliphatic ester groups.