Crystallization kinetics and nucleation activity of silica nanoparticle-filled poly(ethylene 2,6-naphthalate)

Silica nanoparticle-filled poly(ethylene 2,6-naphthalate) (PEN) composites were melt-blended to improve the mechanical and rheological properties of PEN. The melt viscosity and total torque values of the composites were reduced by the silica content. The crystallization exothermic peak shifted to a higher temperature, and the overall crystallization time was reduced by increasing the silica content. Non-isothermal crystallization kinetics was analyzed using the Ozawa and Avrami theories, and a combined method. The combined method was successful in describing the non-isothermal crystallization of these composites. The crystallization activation energy calculated using Kissingerʹs method was reduced, and the spherulite growth rate increased, with increasing silica content. y of the nucleation activity, which indicated the influence of the filler on the polymer matrix, revealed that the fumed silica nanoparticles had a good nucleation effect on PEN.