Polymer/silicate nanocomposites synthesized with potassium persulfate at room temperature: polymerization mechanism, characterization, and mechanical properties of the nanocomposites

Polymer/silicate nanocomposites were synthesized using potassium persulfate (KPS) in the presence of silicate and 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS) without exterior redox co-catalysts at a room temperature. A mechanism for the room temperature polymerization in the presence of silicate was suggested: AMPS attached on the surface of silicate layers would oxidize Fe+2 in silicate lattice to become Fe+3 and the Fe+3 would decompose KPS to form radicals like redox co-catalysts. Poly (acrylonitrile) (PAN)/silicate nanocomposite showed an exfoliated structure, but poly (methyl methacrylate) (PMMA)/silicate nanocomposite showed an intercalated structure. Polymers recovered from the nanocomposites synthesized at a room temperature had high isotactic configurations compared to bulk polymers. The dipole–dipole interaction between monomers and silicate surface might make the lamella of monomers to form on the silicate layer surface and produced polymers with more isotactic configurations. PAN/silicate nanocomposite showed two glass transition temperatures at 113 and 151 °C. The lower temperature might be related to the molecules with low molecular weight. PMMA/silicate nanocomposite had a storage modulus of 4.47×109 Pa at 40 °C.