Amelioration of mechanical brittleness in hyperbranched polymer. 1. Macroscopic evaluation by dynamic viscoelastic relaxation

Hyperbranched poly(ether ketone)-b-linear poly(ether ketone)-b-hyperbranched poly(ether ketone) (HLHPEK) triblock copolymers with two different block compositions were prepared as an approach to improve the mechanical brittleness of hyperbranched poly(ether ketone) (HPEK). From the time–temperature superposition of dynamic shear moduli, G′(ω) and G″(ω), of HPEK and two HLHPEKs, it was investigated that the junction points between G′(ω) and G″(ω) shifted to the higher frequencies and the rubbery plateau region spread wider over the reduced frequency axis as the linear blocks were introduced and their compositions were increased. Such changes in viscoelastic response were consequences of increase in the amount of chain entanglements additionally formed by the linear blocks. In order to verify the effect of the linear block incorporation on amelioration of the mechanical brittleness, the degree of brittleness and its improvement were evaluated from the temperature dependence of the shift factors, aTs, experimentally obtained during the superposition of the dynamic moduli and of the average viscoelastic relaxation times, τHNs, determined with empirical Havriliak–Negami distribution function. From the nonlinear curve fittings of the aTs and the τHNs by the Vogel–Tamman–Fulcher equation, the degree of brittleness for HPEK and HLHPEK triblock copolymers were quantified as values of the material parameter D, an indicative of deviation from the linear Arrhenius behavior and a measure of fragility of the given material. The tendency of increasing D values with the linear block compositions confirmed substantial improvement of the mechanical brittleness in the HLHPEK triblock copolymers compared to HPEK. Therefore, the approach to copolymerize HPEK with its chemically analogous linear counterpart was verified to be an effective strategy to impart molecular entanglements and hence ameliorate the mechanical brittleness on the basis of macroscopic rheological evaluation.