ATRP of (meth)acrylates initiated with a bifunctional initiator bearing trichloromethyl functional groups and structural analysis of the formed polymer

ATRP of methyl methacrylate (MMA), initiated with 1,3-bis{1-methyl-1-[(2,2,2-trichloroethoxy)carbonylamino]ethyl}benzene as a bifunctional initiator (BI) under CuCl catalysis was studied in the presence of 2,2′-bipyridine (bpy) or hexamethyltriethylenetetramine (HMTETA) ligands, in bulk or in toluene. With the bpy, the polymerization reaches only limited monomer conversions and products have broad MWDs. In contrast, polymerization in the presence of HMTETA is a well-controlled process, affords virtually quantitative conversion, giving PMMAs with narrow MWDs and predictable molecular weights within a range of more than one order of magnitude. NMR analysis of the prepared PMMA proved formation of linear polymers with im-measurable extent of chain branching or β-scission as undesired side reactions. The prepared α,ω-dichloro-PMMAs were used as macroinitiators for ATRP of tert-butyl acrylate (t-BuA), giving the corresponding triblock copolymers with narrow MWDs and molecular weights controllable in a wide range. Block copolymerizations were performed in dimethyl formamide (DMF) or acetone in the presence of pentamethyldiethylenetriamine (PMDETA) as ligand and could be accelerated by addition of metallic copper.