Intercalation and viscoelasticity of poly(ether-block-amide) copolymer/montmorillonite nanocomposites: Effect of surfactant

A poly(ether-block-amide) copolymer (PEBA) was successfully hybridized with montmorillonites using melt processing techniques to form nanocomposites. The organoclays used in preparation of the nanocomposites were modified with ammonium surfactants of different molecular structures to study the effect of the surfactant on the intercalation and exfoliation of the polymer by X-ray diffraction (XRD) and dynamic linear viscoelastic analysis. The polymer was found to be capable of forming intercalated composite with unmodified montmorillonite and the best intercalation and exfoliation was found in the hybrids using surfactants that possess hydroxyl group. Organoclays modified with a single tallow tail ammonium prevailed over those modified with a double tallow tail ammonium in intercalation and exfoliation of silicate layers. Higher capacity of ion exchange also led to a better intercalation for hybrids using single tail surfactants, but the hybrids with swallow tail surfactant behaved oppositely. XRD data showed that the diffraction peaks in the hybrids were narrower than those of the organoclay implying a higher order and more number of layers in the stacks of clays. The intercalation of nanocomposites was found dominated by the energetic factor and entropic factor played no role in the outcome of intercalation. Results of linear viscoelastic measurements paralleled those of XRD showing that melts of those nanocomposites with a superior intercalation or exfoliation also exhibited higher storage modulus and thus the linear viscoelasticity could be an indicator for intercalation. The composites showed an abnormal terminal behavior suggesting the existence of a network structure.