Effects of high molecular weight component on crystallization of polyethylene under shear flow

Crystallization of polyethylene (PE) blends of low and high molecular weight components under shear flow was studied using time-resolved depolarized light scattering (DPLS), focusing on effects of the high molecular weight component on the shish–kebab structure formation. Anisotropic two-dimensional scattering pattern due to shish-like structure formation was observed above a certain concentration of the high molecular weight PE. The threshold was about 2.5–3 times larger than the chain overlap concentration, suggesting an important role of entanglements of the high molecular weight component. On the basis of these results a gel-spinning-like mechanism for the shish-like structure formation has been proposed. The DPLS results also implied that the shish-like structure was mainly formed from the high molecular weight PE. This was confirmed by small-angle neutron scattering (SANS) and small-angle X-ray scattering (SAXS) measurements on an elongated PE blend of low molecular weight deuterated PE and high molecular weight hydrogenated PE (3 wt%).