Effect of carboxylic acid monomer and butadiene on particle growth in the emulsifier-free emulsion copolymerization of styrene–butadiene–carboxylic acid monomer

Carboxylated styrene–butadiene rubber (XSBR) latexes were prepared by emulsifier-free batch emulsion copolymerization of styrene and butadiene with different types of carboxylic acid monomers (AA, MAA, IA). It was found that the particle growth is dependent on the hydrophilic nature of carboxylic acid monomers. SEM studies showed that Np is almost constant in the particle growth stage (conversion above 10%). Through some calculations by data obtained from DLS technique, average diameter of monomer swollen polymer particles of all the XSBR latexes at the same conversion of 0.4 was obtained to be 368.91, 174.17 and 437.15 nm for AA, MAA and IA, respectively. Several kinetic parameters related to the particle growth stage such as the average number of growing chain per particle were calculated to be 0.474, 0.370 and 1.685 for AA, MAA and IA, respectively. It was observed that these kinetic parameters increase with increasing average diameter of monomer swollen polymer particles, which is consistent with the emulsion polymerization kinetics. Moreover, results indicated that the polymerization rate per particle or equivalently the average number of the growing chain per particle (particle growth stage) decreases by replacing a part of styrene with butadiene in the emulsion copolymerization recipe of styrene–carboxylic acid monomer.